Nitride semiconductor substrate and method of producing same

Abstract

A nitride semiconductor crystal substrate is produced by forming a network mask repeating a closed loop unit shape upon an undersubstrate, growing a nitride semiconductor crystal in vapor phase, producing convex facet hills covered with facets on exposed parts Π, forming outlining concavities on mask-covered parts, not burying the facets, maintaining the convex facet hills on Π and the network concavities on, excluding dislocations in the facet hills down to the outlining concavities on, forming a defect accumulating region H on, decreasing dislocations in the facet hills and improving the facet hills to low defect density single crystal regions Z, producing a rugged nitride crystal, and slicing and polishing the nitride crystal into mirror nitride crystal wafers. After the fabrication of devices on the nitride wafer, dry-etching or wet etching of hot KOH or NaOH divides the device-carrying wafer into chips by corroding the network defect accumulating region H.