Pattern independent si:c selective epitaxy

Abstract

Trenches are formed in a silicon substrate by etching exposed portions of the silicon substrate. After covering areas on which deposition of Si:C containing material is to be prevented, selective epitaxy is performed in a single wafer chamber at a temperature from about 550° C. to about 600° C. employing a limited carrier gas flow, i.e., at a flow rate less than 12 standard liters per minute to deposit Si:C containing regions at a pattern-independent uniform deposition rate. The inventive selective epitaxy process for Si:C deposition provides a relatively high net deposition rate a high quality Si:C crystal in which the carbon atoms are incorporated into substitutional sites as verified by X-ray diffraction.