Preparation method of branched polyamide (pa) copolymer with ultra-high toughness, pa copolymer prepared using the method, and use of the pa copolymer

Abstract

A preparation method of a branched polyamide copolymer with ultra-high toughness is disclosed. The preparation method includes: (1) dissolving a linear dibasic acid in a solvent A to obtain a linear dibasic acid solution, dissolving a diamine B in a solvent B to obtain a diamine solution B, and dissolving a diamine C in a solvent C to obtain a diamine solution C; (2) adding the diamine solution B to the linear dibasic acid solution to obtain an amide salt solution B; and adding the diamine solution C to the linear dibasic acid solution, and collecting a precipitate to obtain an amide salt C; and (3) mixing the amide salt solution B with the amide salt C, adding a catalyst, and conducting melt polycondensation. The prepared branched copolymer has excellent mechanical performance and is suitable for melt blending toughening, melt extrusion spinning, blow-extruded films, hot melt adhesives, and other fields.