Silicon carbide semiconductor device and method of manufacturing silicon carbide semiconductor device

Abstract

After a titanium nitride film is formed to cover an interlayer insulating film, a first nickel film is formed on a front surface of a silicon carbide base exposed in a contact hole, so as to extend on the titanium nitride film. Next, the silicon carbide base and the first nickel film are reacted by rapid thermal annealing at a temperature of 800 to 1100 degrees C. to form a nickel silicide film that forms an ohmic contact. Grains of the titanium nitride film are enlarged by the rapid thermal annealing, making a grain size of the titanium nitride film 20 nm to 50 nm. Thus, interstices of the grains of the titanium nitride film become smaller than before the rapid thermal annealing or are eliminated, enabling the intrusion of nickel from the first nickel film into the interstices of the columnar grains of the titanium nitride film to be suppressed.