A system for depositing a film on a substrate in a CVD process has a second-source injection sub-system for injecting a control gas. The deposition rate of the material deposited in the CVD process is a function of the concentration of the control gas at the point that material is deposited. The second source injection sub-system provides a concentration gradient of the control gas relative to the substrate surface coated, and alters the thickness uniformity of the film. By controlling the gradient one may control the thickness uniformity profile. In another embodiment, the invention applies to dry etching with reactive gas, and the etching rate is controlled by second source provision of a control gas.

Film uniformity by selective pressure gradient control

A chemical vapor deposition process performed at a temperature below 440 degrees C. for blanket tungsten deposition as a step in manufacturing integrated circuits deposits an integrated film suitable for voidless fill of vias as small as 0.5 microns in width and with aspect ratios of more than 2, while providing resistivity well below 100 micro-ohms per square, film stress generally in the mid 7E+09 dynes per square centimeter and below, and reflectivity of more than 40%, measured relative to silicon at 436 nanometer wavelength for 1 micron film thickness, while avoiding the use of nitrogen in the process.

Growing community of inventors

San Ramon, CA, United States of America

Edward J Rode