The patent badge is an abbreviated version of the USPTO patent document. The patent badge does contain a link to the full patent document.
The patent badge is an abbreviated version of the USPTO patent document. The patent badge covers the following: Patent number, Date patent was issued, Date patent was filed, Title of the patent, Applicant, Inventor, Assignee, Attorney firm, Primary examiner, Assistant examiner, CPCs, and Abstract. The patent badge does contain a link to the full patent document (in Adobe Acrobat format, aka pdf). To download or print any patent click here.
Patent No.:
Date of Patent:
Aug. 18, 1987
Filed:
Apr. 11, 1986
Klaus Hunold, Lauben, DE;
Alfred Lipp, Bad Worishofen, DE;
Klaus Reinmuth, Durach, DE;
Peter Arnold, Sulzberg, DE;
Johannes Napholcz, Kempten, DE;
Elektroschmelzwerk Kempten GmbH, Munich, DE;
Abstract
The invention is a process for the manufacture of shaped articles of reaction-bonded silicon nitride in which pre-shaped articles of silicon powder are heated in a first stage under a nitrogen gas pressure of at least 6 MPa at a heating rate of not more than 50.degree. C. per hour to a reaction temperature below the melting point of silicon, the article is maintained at the reaction temperature for at least 0.5 hours and subsequently, in a second stage, heating the article at a heating rate of at least 500.degree. C. per hour to a temperature above the melting point of silicon and maintaining the article at that temperature for from 1 to 7 hours. The process can nitridate both pre-shaped articles consisting of silicon powder and, optionally, up to 15% by weight Si.sub.3 N.sub.4 powder and those containing up to 10% by weight of a sintering aid such as Y.sub.2 O.sub.3. In the former case, porous shaped articles having a density of from 87 to 91% TD and, in the latter case, dense shaped articles having a density of more than 98% TD, are obtained. In all cases, in a total nitridation time of less than 15 hours, a conversion of at least 95% of the silicon originally present into silicon nitride is achieved, which, in the finished shaped article, is substantially in the .beta.-modification.