Silica bricks and method for manufacturing silica bricks

Abstract

Present invention provides silica bricks of improved thermal conductivity and low gas permeability and method for manufacturing such silica bricks. The manufacturing method is substantially characterized in that siliceous raw mixture includes 0.5 to 10 percent by weight of nitride or carbide of metallic silicon and that, in the firing process from 1200.degree. to 1400.degree. C., the temperature elevation speed and the oxygen concentration at the exhaust port of the firing furnace take specific rates respectively different from the corresponding rates of conventional firing. In the above firing process, the nitride or carbide of metallic silicon is oxidized to form SiO.sub.2 and this SiO.sub.2 fills in pores of the matrix whereby silica bricks produced by the method of this invention can have high thermal conductivity and low gas permeability.