Wire rod for 5000 mpa-grade diamond wire and production method therefor

Abstract

A wire rod for a 5000 MPa-grade diamond wire and a production method are provided. The wire rod includes the following chemical components: 1.01% to 1.1% of carbon, 0.15% to 0.4% of silicon, 0.3% to 0.6% of manganese, 0.01% to 0.4% of chromium, 0.0005% to 0.002% of boron and/or 0.01% to 0.09% of vanadium; and the balance of iron and impurities. The production method includes vacuum melting, electroslag remelting and/or vacuum consumable melting, grinding after cogging/forging, high-speed wire rolling and cooling, and cogging at 1030° C. to 1060° C. The wire rod, with structural uniformity and tensile strength of more than or equal to 1320 MPa, can be configured to prepare 5000 MPa-grade steel wires with a diameter of 40 μm to 46 μm.