Steel sheet with excellent bake hardening properties and corrosion resistance and method for manufacturing same

Abstract

Provided is a steel sheet by weight percentage (wt %), carbon (C): 0.005 to 0.08%, manganese (Mn): 1.25% or less (excluding 0%), phosphorus (P): 0.03% or less (excluding 0%), sulfur (S): 0.01% or less (excluding 0%), nitrogen (N): 0.01% or less (excluding 0%), soluble aluminum (sol.Al): 0.01 to 0.06%, chromium (Cr): 1.15 to 2.5%, antimony (Sb): 0.1% or less (excluding 0%), at least one selected from the group consisting of nickel (Ni): 0.3% or less (excluding 0%), silicon (Si): 0.3% or less (excluding 0%), molybdenum (Mo): 0.2% or less (excluding 0%), and boron (B): 0.003% or less (excluding 0%), and a remainder of iron (Fe) and other unavoidable impurities, satisfying Expression 1: 1.3≤Mn(wt %)+Cr(wt %)/1.5+Sb(wt %)≤2.7, where Mn, Cr, and Sb refer to contents (wt %) of corresponding elements, respectively; and 1 to 5% of martensite and a remainder of ferrite by an area percentage (area %).