Method of preparing mof-coated monocrystal ternary positive electrode material

Abstract

The present invention provides a method of preparing an MOF-coated monocrystal ternary positive electrode material. Firstly, a solution A of nickel, cobalt and manganese metal salts, an ammonia complexing agent solution and a caustic soda liquid are added to a reactor for reaction to obtain a precursor core; then, an organic carboxylate is dissolved in an amount of an organic solvent to obtain a solution B; the solution B and a manganese metal salt solution with a given concentration are added to the reactor and aged to obtain an MOF-coated core-shell structure precursor; the core-shell structure precursor is pre-sintered at a low temperature to obtain a nickel-cobalt-manganese oxide with monocrystal structure; the nickel-cobalt-manganese oxide with monocrystal structure is uniformly mixed with LiOH·HO in a mortar and then calcined at a high temperature to obtain an MOF-coated monocrystal ternary positive electrode material.