The patent badge is an abbreviated version of the USPTO patent document. The patent badge does contain a link to the full patent document.
The patent badge is an abbreviated version of the USPTO patent document. The patent badge covers the following: Patent number, Date patent was issued, Date patent was filed, Title of the patent, Applicant, Inventor, Assignee, Attorney firm, Primary examiner, Assistant examiner, CPCs, and Abstract. The patent badge does contain a link to the full patent document (in Adobe Acrobat format, aka pdf). To download or print any patent click here.
Patent No.:
Date of Patent:
Nov. 23, 2021
Filed:
Sep. 15, 2020
University of Science and Technology Beijing, Beijing, CN;
Jinfeng Huang, Beijing, CN;
Jin Zhang, Beijing, CN;
Cheng Zhang, Beijing, CN;
Chao Zhao, Beijing, CN;
Yong Lian, Beijing, CN;
Jianqiang Li, Beijing, CN;
Cheng Zhang, Luoyang, CN;
University of Science and Technology Beijing, Beijing, CN;
Abstract
The present application provides a hot-work die steel and a preparation method thereof wherein the chemical constituents of the hot-work die steel in mass percentage are as follows: C: 0.20-0.32 wt %, Si: ≤0.5 wt %, Mn: ≤0.5 wt %, Cr: 1.5-2.8 wt %, Mo: 1.5-2.5 wt %, W: 0.5-1.2 wt %, Ni: 0.5-1.6 wt %, V: 0.15-0.7 wt %, Nb: 0.01-0.1 wt %, and a balance of iron, wherein an alloying degree is 5-7%; a tensile strength of the hot-work die steel at 700° C. is 560-700 MPa; a value of hardness of the hot-work die steel at room temperature is 32-38 HRC after holding at 700° C. for 3-5 h; and the hot-work die steel has an elongation of 14% to 16% at room temperature, a percentage reduction of area of 48% to 65%, and an impact toughness of 52-63 J at room temperature. The hot-work die steel of the present application has an excellent thermal stability as well as a good plasticity and a toughness at room temperature.