A cleavage method of bisphenols capable of yielding a product containing high-purity isopropenylphenol and phenol is disclosed, including (1) a cleavage step of supplying the mixture containing bisphenols together with chroman derivatives and flavan derivatives formed as by-products in the production process of bisphenols to a cleaving vessel and carrying out a cleavage reaction in the presence of a basic or acidic catalyst at a temperature of from 150 to 260&deg; C. under a reduced pressure condition of not higher than 300 mmHg, (2) a distillation step of supplying the cleavage step product formed in the cleavage step in a vapor state to a distillation column and distilling at a temperature of from 130 to 200&deg; C. under a reduced pressure condition of not higher than 300 mmHg, and (3) a reflux step of condensing the distillate from the distillation step, refluxing a part thereof to the distillation step at a reflux ratio of from 0.01 to 3, and discharging out the residue from the system.

Cleavage method of bisphenols

A preparation process of phenol aralkyl resin from phenol compound and aralkyl compound by controlling the temperature of reaction mass in the range of 70 to 240.degree. C. and simultaneously controlling the temperature of vapor phase potion and vapor-liquid interface portion of manufacturing equipment so as to keep the wall surface of the vapor phase portion and vapor-liquid interface portion in a wet state. The invention can prevent scale adhesion to the interior of manufacturing equipment, remarkably reduce the number of washing and scale removing procedures on the manufacturing equipment, and enable efficient manufacture of phenol aralkyl resin. When the phenol aralkyl resin obtained is used for a molding material, molded articles having excellent heat resistance and high reliability can be provided.

Preparation process of phenol aralkyl resins

A random-block copolymer having appropriate hydrolyzability, excellent flexibility and excellent mechanical strength, a monofilament thereof, and a process for producing the copolymer. The random-block copolymer comprises from 5 to 50 mol % of a random copolymer segment containing from 20 to 80 mol % of a lactide unit (A) and from 80 to 20 mol % of a caprolactone unit (B), and from 95 to 50 mol % of a block copolymer segment containing a glycolide unit (C).

Random-block copolymer and monofilament thereof

A method for the homopolymerization or copolymerization of vinyl chloride, wherein the inner wall of the polymerizer and the like are prevented from being fouled with the resulting polymer by applying a coating fluid containing the oxidative polymerization product of a specific phenolic monomer to the surface of the inner wall of the polymerizer and the like, as well as an anti-fouling agent used for this purpose. The method of this invention can very effectively prevent the polymerizer and the like from being fouled with the resulting polymer without affecting the polymerization rate and various properties of the product. Consequently, the necessity of performing the operation for removal of the deposited polymer after completion of each polymerization cycle is eliminated, thus making it possible to achieve closed polymerization requiring no manhole opening after each polymerization cycle which is becoming increasingly popular in recent years.

Method for preventing the inner wall surfaces of the polymerization