The invention provides a method for making Zr alloy nuclear reactor fuel cladding having excellent corrosion resistance and creep properties. The method includes performing hot forging, solution heat treatment, hot extruding, and repeated cycles of annealing and cold rolling of a Zr alloy including, by weight, 0.2 to 1.7% Sn, 0.18 to 0.6% Fe, 0.07 to 0.4% Cr and 0.05 to 1.0% Nb, with the remainder being Zr and incidental impurities, and the incidental nitrogen impurity content being 60 ppm or less, and then performing final stress relief annealing thereon. The annealing is performed at a temperature of 550.degree. C. to 850.degree. C. for 1 to 4 hours such that the accumulated annealing parameter .SIGMA.Ai=.SIGMA.ti.multidot.exp(-40,000/Ti) satisfies relationships -20.ltoreq.log.SIGMA.Ai.ltoreq.-15, and -18-10.multidot.X.sub.Nb .ltoreq.log.SIGMA.Ai.ltoreq.-15-3.75.multidot.(X.sub.Nb -0.2), wherein Ai represents the annealing parameter for the i-th annealing, ti represents the annealing time (hours) for the i-th annealing, Ti represents the annealing temperature (K) for the i-th annealing, and X.sub.Nb represents the Nb concentration (wt %).

Method for making Zr alloy nuclear reactor fuel cladding having

A fuel rod for a light water reactor comprises a cladding tube which comprises a zirconium alloy having a composition including 0.6 to 2.0% by weight of Nb, 0.5 to 1.5% by weight of Sn, 0.05 to 0.3% by weight of Fe, and the balance being Zr and incidental impurities; uranium oxide fuel pellets packed in the cladding tube; and end plugs comprising a zirconium alloy and closing both ends of the cladding tube. The cladding tube is sealed by TIG welding with the end plugs. Grain boundaries in each heat affected zone of the cladding tube, which are adjacent to a bead formed by TIG welding, have structural compositions including 4 to 30% by weight of Nb, and 0.9 to 20% by weight of Fe.

Fuel rod for light water reactor and method for manufacturing the same

A fuel rod for a light water reactor comprises a cladding tube which comprises a zirconium alloy having a composition including 0.6 to 2.0% by weight of Nb, 0.5 to 1.5% by weight of Sn, 0.05 to 0.3% by weight of Fe, and the balance being Zr and incidental impurities; uranium oxide fuel pellets packed in the cladding tube; and end plugs closing both ends of the cladding tube. The cladding tube is sealed by TIG welding with the end plugs. Precipitates having grain diameters of 0.01 to 0.5 .mu.m and comprise intermetallic compounds containing Zr, Nb and Fe are present at grain boundaries in the structure of heat affected zones of the cladding tube, the heat affected zone being adjacent to a bead formed by TIG welding.

A corrosion resistant zirconium alloy for use as a nuclear reactor cladding material. This alloy consists essentially of, on a weight % basis 0.02-1.7 % Sn, 0.19-0.6% Fe, 0.07-0.4% Cr, 0.01-0.2% Ta, and optionally 0.05 up to less than 0.5% Nb, the balance being Zr and incidental impurities, provided that the content of the nitrogen in the form of incidental impurities is no more than 60 ppm.

Highly corrosion-resistant zirconium alloy for use as nuclear reactor

A corrosion resistant zirconium alloy for use as a nuclear reactor cladding material. This alloy consists essentially of, on a weight % basis 0.02-1.15% Sn, 0.19-0.6% Fe, 0.07-0.4% Cr, and optionally 0.05 to not more than 0.5% Nb, the balance being Zr and incidental impurities, provided that the content of the nitrogen in the form of incidental impurities is no more than 60 ppm.