The present disclosure provides a transparent alumina-based plate, and a hot-pressing method to make the transparent alumina-based plate from platelet alumina. Alumina powder with a platelet morphology was hot-pressed to transparency with pre-load pressures of about 0-8 MPa, maximum temperatures of about 1750-1825° C., maximum pressures of about 2.5-80 MPa, and isothermal hold times of 1-7 hours. A novel alumina-based plate has been prepared, wherein the plate has a thickness of 2-5 mm, an in-line transmission of at least 60-75% for a light with a wavelength range of 645-2500 nm, an in-line transmission variance of <15% over the wavelength range of 645-2500 nm, and a relative density of 99.00-99.95%.