Ford Motor Company Limited

Walter J Evans

Adolf Hetke

Chia M Yen

An aluminum casting alloy consisting of, by weight, of 7.0-13.0% copper, 0.4-1.2% manganese, 0.21-40% vanadium, 0.31-0.70% zirconium; impurities limited to: less than to 0.6% Si, less than 0.8% Fe, less than 0.2% zinc, less than 0.1% Mn, less than 0.2% Ni, and the remainder being essentially aluminum. There is an absence of titanium, cobalt, molybdenum, tungsten, chromium, boron, tantalum, and niobium. The alloy has, at room temperature, a UTS of about 61 ksi, a YS of about 49 ksi, a tensile elongation of about 6%, and tensile modulus elasticity of about 11.5 MSI, a compressive yield strength of about 53 ksi, a compressive modulus of elasticity of about 18 MSi; high temperature physical properties at 500.degree. F., after 1000 hours exposure to 500.degree. F., comprise a tensile strength of 33 ksi or greater, a tensile yield strength of 23 ksi or greater, a tensile elongation of about 9%, and tensile modulus of elasticity of 10 msi. The alloy is fabricated by a) squeeze casting an aluminum alloy melt of such character; (b) extracting the solidified casting from the die and heat treating the casting to dissolve all alloying elements (i.e., 995.degree.-1018.degree. F. for 7-20 hours); and (c) aging the solution treated casting to achieve improved strength characteristics (i.e., in the range of 340.degree.-400.degree. F. for 5-20 hours).

Aluminum casting alloy for high strength/high temperature applications

An aluminum casting alloy consisting of, by weight, of 7.0-13.0% copper, 0.4-1.2% manganese, 0.21-0.40% vanadium, 0.31-0.70% zirconium; impurities limited to: less than to 0.6% Si, less than 0.8% Fe, less than 0.2% zinc, less than 0.1% Mn, less than 0.2% Ni, and the remainder being essentially aluminum. There is an absence of titanium, cobalt, molybdenum, tungsten, chromium, boron, tantalum, and niobium. The alloy has, at room temperature, a UTS of about 61 ksi, a YS of about 49 ksi, a tensile elongation of about 6%, and tensile modulus elasticity of about 11.5 MSi, a compressive yield strength of about 53 ksi, a compressive modulus of elasticity of about 18 MSi; high temperature physical properties at 500.degree. F., after 1000 hours exposure to 500.degree. F., comprise a tensile strength of 33 ksi or greater, a tensile yield strength of 23 ksi or greater, a tensile elongation of about 9%, and tensile modulus of elasticity of 10 msi. The alloy is fabricated by a) squeeze casting an aluminum alloy melt of such character; (b) extracting the solidified casting from the die and heat treating the casting to dissolve all alloying elements (i.e., 995.degree.-1018.degree. F. for 7-20 hours); and (c) aging the solution treated casting to achieve improved strength characteristics (i.e., in the range of 340.degree.-400.degree. F. for 5-20 hours).

A method of treating molten metals is disclosed which employs a solid sheathless flexible strand containing particles of the treating agent uniformly suspended in a binder matrix, the latter being consumable or vaporizable upon contact with molten metal. Positive and predetermined solution conditions of the treating agent are assured by regulating the molten metal flow velocity to be at or above a predetermined minimum and the strand injection rate to be within defined limits.

Growing community of inventors

Canton, MI, United States of America

Walter J Evans