Provided is a polycarbonate resin composition, including: an aromatic polycarbonate resin (A); an alicyclic epoxy compound (B); a predetermined antioxidant (C); and a predetermined phosphorus compound (D), wherein, with respect to 100 parts by mass of the component (A), a content of the component (B) is 0.01 part by mass or more and 0.1 part by mass or less, a content of the component (C) is 0.01 part by mass or more and 0.1 part by mass or less, and a content of the component (D) is 0.01 part by mass or more and 0.05 part by mass or less.

Polycarbonate resin composition and molded body

Provided is an aromatic polycarbonate resin composition, including, with respect to 100 parts by mass of an aromatic polycarbonate resin (A), 0.01 part by mass to 0.1 part by mass of an alicyclic epoxy compound (B), 0.2 part by mass to 0.6 part by mass of a polyether compound (C) having a polyoxyalkylene structure, and 0.005 part by mass to 1 part by mass of a phosphorus-based compound (D), wherein a difference between a YI value of a 5-millimeter thick molded body, which is obtained by molding the aromatic polycarbonate resin composition at 320&#xb0; C., after a lapse of 3,000 hours under an environment at 85&#xb0; C. and a humidity of 85%, and an initial YI value thereof is 3.0 or less.

Aromatic polycarbonate resin composition and optical molded article

Provided is a polycarbonate resin composition, including, with respect to 100 parts by mass of an aromatic polycarbonate resin (A), 0.005 part by mass to 1 part by mass of a phosphorus-based compound (B) having an aryl group, and 0.005 part by mass to 5 parts by mass of a polyether compound (C) having a specific polyoxyalkylene structure, in which: an amount of a compound having a phenol structure produced by decomposition of the phosphorus-based compound (B) 1,500 hours after standing thereof under conditions of 40&#xb0; C. and a humidity of 90% is 5 mass % or less with respect to the phosphorus-based compound (B); and when a weight of the phosphorus-based compound (B) is measured with a thermogravimetric-differential thermal analysis machine under a nitrogen atmosphere, a temperature at which the weight becomes smaller than the weight before the measurement by 2% is 340&#xb0; C. or more.

Polycarbonate resin composition

Provided is a polycarbonate resin molding material, including an aromatic polycarbonate resin (A), in which the polycarbonate resin molding material has: a content of o-hydroxyacetophenone measured by a predetermined method (1) of 1 ppm by mass or less; and a YI value measured by a predetermined method (2) of 1.21 or less.

Polycarbonate resin molding material

Provided is an aromatic polycarbonate resin molded body, which is obtained by molding a resin molding material containing an aromatic polycarbonate resin (A), in which: the molded body has a thin-walled portion having a thickness of 0.5 mm or less; the molded body has an o-hydroxyacetophenone content of 1 ppm by mass or less and a nitrogen atom content of 15 ppm or less; and the molded body is free of an absorption maximum in a wavelength range of from 500 nm to 600 nm.