The present invention relates to cellulose fiber containing 500 to 2000 of filaments and having homogeneous physical properties and the multi-filaments according to the present invention is characterized in that the strength and the breaking elongation of the multi-filaments are 4 to 9 g/d and 4 to 15%, respectively. In particular, the present invention is characterized in that each mono-filament selected 100 strands from every three part divided from multi-filaments has properties as following: (a) 3 to 9 g/d in average strength, 7 to 15% in average breaking elongation and 0.035 to 0.055 in by birefringence, (b) the differences of the above three parts are below 1.0 g/d in average strength, 1.5% in breaking elongation and 0.7 denier in denier, (c) the CV (%) (coefficient of variation) of the above three parts are below 10%, and (d) the birefringence differences of the above three parts are below 0.004.

Cellulose multi-filament

Cellulose fiber for using as industrial materials

This invention relates to a method of preparing cellulose solution which is homogeneous at relatively low temperature, in which a small amount of cellulose powder or polyvinylalcohol is dissolved in the liquid-state, concentrated N-methylmorpholine-N-oxide (hereinafter, referred to as 'NMMO') so as to lower the solidifying temperature of NMMO, and then, the resulting solution and cellulose powder are fed into an extruder so as to be mixed, swollen and melted in the extruder.

Solution containing cellulose dissolved in N-methylmorpholine-N-oxide and high tenacity lyocell multifilament using the same

The present invention relates to a method for making highly homogenized cellulose solution, wherein the cellulose solution is obtained by obtaining a solidified N-methylmorphorine-N-oxide (hereinafter, referred to as 'NMMO') hydrates which is solidified a liquid-state NMMO hydrates comprising 10 to 18% by weight water by using a simple screw-type feeder and by controlling the temperature, feeding the solidified NMMO into a twin-screw type extruder continuously, obtaining a cellulose solution which is fully swelled in a few minutes by dispersing and mixing with cellulose powder in the twin-screw type extruder, and extruding a highly homogenized cellulose solution by feeding the obtained cellulose solution into a melting zone of the extruder to melting the cellulose solution in a few minutes by minimum heat and shear force.

Homogeneous cellulose solution and high tenacity lyocell multifilament using the same

The present invention relates to, and more particularily, to a lyocell dip cord and tire produced by a method comprising the steps of: (A) dissolving 0.01 to 3 wt % of cellulose powder in portions in concentrated liquid N-methylmorpholine N-oxide (NMMO) to prepare cellulose-containing NMMO solution; (B) feeding the NMMO solution and cellulose powder into an extruder having a screw to be subjected to dispersing, mixing, shearing, kneading, melting and measuring ability in the extruder to prepare a swollen and homogenized cellulose solution; (C) spinning the cellulose solution through a spinning nozzle, passing the spinning solution through an air gap to a coagulation bath and coagulating the spinning solution to obtain a multifilament; (D) subject the multifilament to water-wash, drying and oil-treatment, followed by winding; and (E) twisting the wound yarn with a twisting machine to prepare a greige cord, weaving the greige cord and dipping the woven cord in a dipping solution.

Cellulose dip cord produced from highly homogeneous cellulose solution and tire using the same

The present invention relates to a high tenacity, high modulus and low shrinkage lyocell multifilament yarn suitable for use in tire cords and MRG (mechanical rubber goods). The lyocell multifilament yarn is a cellulose-based fiber for industrial applications, which is produced by dissolving pulp having a degree of polymerization (DP) of 700-2,000 and preferably 800-1,400, and a &#x3b1;-cellulose content of more than 90% and preferably more than 92%, in N-methylmorpholine N-oxide (NMMO) hydrate, at a pulp concentration of 5-15% by weight and preferably 8-13% by weight. The lyocell monofilament according to the present invention is characterized by the following stress-strain profile: (1) the lyocell monofilament analyzed after drying is elongated by less than 3.0% and has an initial modulus of 150-400 g/d, when it was subjected to an initial stress of 3.0 g/d; (2) it is elongated by 3.0-7.0% when it was subjected to a stress greater than the initial stress but smaller than 6.0 g/d; and (3) it is elongated from a tensile tenacity of at least 6.0 g/d until the yarn is broken.