A double-inverse opal photonic crystal resin film is formed by embedding nanospheres in pores of polyacrylate inverse opal framework material and then filling the pores of the double-inverse opal photonic crystal resin film with an ethanol solution with hydrophilic acrylamide dissolved therein followed by photopolymerization to form a polyacrylamide network, so as to obtain the double-inverse opal photonic crystal resin film using water as ink. A mass fraction of hydrophilic acrylamide in the ethanol solution is 2 to 8 wt. %. The resin film can induce water to penetrate into the pores of the double-inverse opal photonic crystal resin film, making the nanospheres in the pores of the inverse opal framework distribute from random to order under the action of buoyancy force, thereby eliminating scattering interference and producing brilliant structural colors by regulating refractive index contrast.

Chromogenic double inverse opals photonic crystal resin film using water as ink and the preparation thereof

A bilayer photonic crystal photoswitch thin-film device having the optical characteristics of both 2D and 3D photonic crystals, and a preparation method thereof are provided. When the bilayer photonic crystal photoswitch thin-film device is rotated periodically, different colors can be observed at a fixed rotation angle, that is, the device has the attribute of changing colors by means of rotation, and can thus realize the opening and closing of an optical path. The bilayer photonic crystal photoswitch thin-film new device has broad application prospects in the fields of photoswitches, optical waveguides, optical prisms, warming signs, anti-counterfeiting and information coding, etc.

Bilayer photonic crystal photoswitch thin-film device and preparation method thereof

A structurally stable composite structural chromogenic material and a preparation method thereof are provided. The structurally stable composite structural chromogenic material is formed by stacking a transparent thermoplastic polymer and a structural chromogenic material layer by layer and then thermally bonding the peripheral edges of the polymer into a whole, and the upper surface layer and the lower surface layer of the material are both thermoplastic polymers. The molded composite structure has relatively obvious structural color and good mechanical strength.

Composite structural chromogenic material with stable structure and preparation method therefor

A method for preparing a large-area structural chromogenic pattern by ink-jet printing, a structural chromogenic pattern obtained by the method, and an anti-counterfeiting method based on a structural color change. A dispersion liquid containing mono-disperse colloidal microspheres with high index of refraction is printed onto a piece of paper by using an ink-jet printer, and nano-microspheres are arranged and assembled on the paper to obtain a micro-structure having the features of being ordered from a short distance and disordered from a long distance. A pretty structural color can be observed by means of the interaction of the structure with light, thus displaying a pattern, changing the angle of observation, changing the brightness of the structural color, and hiding and displaying the pattern. The method is simple and convenient, is widely applicable, and can achieve the preparation and anti-counterfeiting of a large-area structural color without external stimulation.

Method for preparing large-area structural chromogenic pattern by ink-jet printing and anti-counterfeiting method based on structural color change

The invention provides a kind of polymer grafted long afterglow phosphor which composed of alkali earth aluminate phosphor grafted by polymer through coordination bond and a method for producing the same. The method for producing a polymer grafted phosphor comprise two steps: the alkali earth aluminate activated by rare earth ions is coordinated with difunctional ligand to form a coordinated long afterglow phosphor; The coordinated long afterglow phosphor was dispersed in organic solvent at 40&#x2dc;130&#xb0; C., the ligand was initiated by initiator and could copolymerize with other polymerizable monomer to form the polymer grafted long afterglow phosphor. The formed phosphors have good water resistance and luminescent properties. They can be widely used in fields of luminescent coatings, paints and plastics.