Nippon Steel Corporation

Shin-ich Teraoka

Masanori Ueda

Hideki Oka

Toshiyuki Suehiro

Yuuji Yoshimura

A process for producing a thin sheet of a Cr-Ni-based stainless steel having excellent surface quality and workability is produced by continuously casting a stainless steel represented by 18%Cr-8%Ni steel by means of a continuous casting machine having a mold wall surface that moves in synchronization with a cast strip, effecting rapid solidification at a cooling rate of 100.degree. C./sec or more into a cast strip having a thickness of 10 mm or less; after solidification thereof, initiating cooling of the cast strip from a high temperature at a rate of 100.degree. C./sec or more to 1250.degree. C. and preventing the occurrence of recuperation; holding the cooled cast strip in a temperature range of from over 900 to 1250.degree. C. exclusive for 5 sec to 2 min; and cooling and coiling the cast strip and subjecting the cast strip to annealing, pickling, cold rolling and annealing.