An investment casting method using a pattern material with substantially spherical filler particulates is used to produce investment cast components with improved surface quality, reduced finishing costs, and reduced core breakage. The pattern material comprises substantially spherical particles within the particle size range of about 10 microns to about 70 microns particle diameter, the use of which reduces the number of random, localized surface depressions and pits to improve pattern surface texture and uniformity. Patterns so formed impart the same improvements to the surface of subsequent investment cast components. The resulting castings exhibit improved as-cast surface finish and reduced random, localized surface pitting, thereby reducing or eliminating expensive post casting surface finishing operations. Moreover, the spherical morphology of the filler particulates reduces injection pressures to fill a pattern die cavity as compared to non-spherical filler particulates. The lower injection pressures eliminate or reduce breakage of ceramic cores positioned in the die cavity for manufacture of hollow cast components, such as internally cooled turbine blades and vanes.

Investment casting with improved as-cast surface finish

The pattern material with substantially spherical filler particulates is used to produce investment cast components with improved surface quality, reduced finishing costs, and reduced core breakage. The pattern material comprises substantially spherical particles within the particle size range of about 10 microns to about 70 microns particle diameter, the use of which reduces the number of random, localized surface depressions and pits to improve pattern surface texture and uniformity. Patterns so formed inpart the same improvements to the surface of subsequent investment cast components. The resulting castings exhibit improved as-cast surface finish and reduced random, localized surface pitting, thereby reducing or eliminating expensive post casting surface finishing operations. Moreover, the spherical morphology of the filler particulates reduces injection pressures to fill a pattern die cavity as compared to non-spherical filler particulates. The lower injection pressures eliminate or reduce breakage of ceramic cores positioned in the die cavity for manufacture of hollow cast components, such as internally cooled turbine blades and vanes.

Growing community of inventors

Muskegon, MI, United States of America

Robert L McCormick