An aluminum alloy plate for an automobile has a chemical composition containing 0.8 to 1.5% by mass of Si, 0.4 to 0.7% by mass of Mg and 0.5 to 0.8% by mass of Cu. The crystal grain size is 10 to 40 &mgr;m. Cu content obtained by analyzing the outermost surface of the aluminum alloy with an oxide film according to X-ray photoelectron spectroscopy (XPS) is {fraction (1/10)} to &frac12; of the Cu content of the bulk of the aluminum alloy plate.

Aluminum alloy plate for automobile and manufacturing method thereof

A core material of an aluminum brazing sheet restricts Mg to less than 0.3 wt % and Fe to not more than 0.2 wt %, and contains more than 0.2 wt % and not more than 1.0 wt % of Cu, 0.3 to 1.3 wt % of Si, 0.3 to 1.5 wt % of Mn and the balance of Al and inevitable impurities. A brazing filler material is formed on one surface of the core material by Al&mdash;Si based aluminum alloy. Also, a cladding material is formed on the other surface of the core material, and contains less than 0.2 wt % of Si, 2.0 to 3.5 wt % of Mg, not less than 0.5 wt % and less than 2.0 wt % of Zn and the balance of Al and inevitable impurities. Further, the value (cladding material hardness)/(the core material hardness) that is a ratio of the hardness of the cladding material to the hardness of the core material is not more than 1.5.

Aluminum brazing sheet

An aluminum alloy composite material for brazing has a core member, an Al--Si filler member clad on one surface of the core member and an aluminum alloy cladding member clad on the other side of the core member. The core member is made of an aluminum alloy containing 0.3 to 1.3 wt. % of Si, 0.3 to 1.5 wt. % of Mn, 0.02 to 0.3 wt. % of Ti, and, as required, 0.3 wt. % or less of Cr and 0.2 wt. % or less of Zr, the content of Mg being restricted to 0.2 wt. % or less and the content of the Cu being restricted to 0.2 wt. % or less as an impurity. The cladding member is made of an aluminum alloy containing 0.3 to 3 wt. % of Mg, 5 wt. % or less of Zn, 0.1 to 1.0 wt. % of Si. The thickness of the core member is preferably, 2.5 times or more greater than that of the filler member, falling within a range of 0.1 to 1 mm. With this, it is possible to obtain an aluminum alloy composite material which cannot degraded in brazability and corrosion resistance even when brazed by the brazing method with noncorrosive flux and which has enough high strength to be used for a material of a high-strength heat exchanger, highly improved corrosion resistance and excellent brazability.

Aluminum alloy composite material for brazing