Thin-walled molded articles (i.e., molded articles where at least 70% of the wall thickness is 0.8 mm or less) are formed of a polybutylene terephthalate (PBT) molding composition having improved fluidity characteristics and desirable mechanical strength properties. The PBT molding composition includes (A) 100 parts by weight of a polybutylene terephthalate base resin having a melt index of between 40 and 200 as measured at 235.degree. C. under a load of 2160 grams according to ASTM D-1238; (B) between 1 to 60 parts by weight of plate-like glass flakes having an average flake dimension of between 10 to 200 .mu.m; and (C) between 0.01 to 5 parts by weight of a fatty acid metal salt.

Polybutylene terephthalate molding composition and molded thin-walled

Self-lubricating polyacetal resin compositions and molded articles (e.g. 'wear parts') formed thereof include a polyacetal base resin, and a self-lubricating effective amount of a silica powder in which a silicone polymer (e.g. silicone oil) is absorbed. The silica powder acts as a carrier for the silicone polymer so as to improve the dispersibility of the silicone polymer in the polyacetal base resin as well as to allow greater silicone polymer 'loading' of the polyacetal base resin. As a result, improved lubricant dispersibility and sliding characteristics are achieved.

Self-lubricated polyacetal molding compositions and molded articles

Polyacetal resin molding compositions and sliding members formed thereof exhibit anti-friction and abrasion-resistance properties. The polyacetal resin molding compositions include (A) 100 parts by weight of a polyacetal base resin, (B) between 0.5 to 40 parts by weight of a branched or cross-linked graft copolymer which is a graft-reaction product of (a) an olefin polymer, and (b) a vinyl or ether polymer, (C) between 0.1 to 20 parts by weight of a lubricant, and (D) between 0.5 to 30 parts by weight of an inorganic powder having a mean particle diameter of 50 .mu.m or less and a content of particles having a particle diameter of 100 .mu.m or less of at least 95%.

Anti-friction and wear-resistant polyacetal molding compositions, and

A self-lubricating wear part is formed of a polyacetal resin composition that includes (A) a polyacetal base resin, (B) an inorganic powder having an average particle diameter of 50 micometers or less, and a particle diameter distribution such that at least 95 percent of the particles have a diameter of 100 micrometers or less and (C) a fatty acid ester. The wear parts are particularly useful for slidable parts such as guide roller or guide pole.