Fuji Electrochemical Co., Ltd.

Michiaki Tsurumi

Kazuaki Endo

Kenji Fujimoto

The present invention provides a dielectric ceramic composition for use in a high-frequency range represented by the general formula (1-x)Ba.sub.1- y(Zn.sub.1/3, Ta.sub.2/3)O.sub.3 +xBa.sub.1-y ZrO.sub.3. In the formula, y is 0.004.ltoreq.y.ltoreq.0.013 and x is the amount of substitution of Ba.sub.1-y ZrO.sub.3 and 0&lt;x.ltoreq.0.06. This composition is prepared by weighing raw materials so that the mixing ratio of Ba is slightly smaller than that of the stoichiometric composition, calcining the resultant mixture to prepare a calcination product, grinding the calcination product through only dry process without conducting wet pulverization, molding the resultant powder, and sintering the molded product at 1600.degree. to 1700.degree. C. for 1 to 10 hr.