Mitsubishi Materials Corporation

Masato Koide

Yutaka Koshiba

Masahiko Wada

Eiho Watanabe

Kiyoyuki Okubo

Takashi Morimoto

Shoji Aoki

Keishi Nogami

A copper wire rod with an excellent surface quality and a magnet wire, in which the occurrence of blister defects is suppressed, are provided. The copper wire rod has a composition consisting of: more than 10 ppm by mass and 30 ppm by mass or less of P; 10 ppm by mass or less of O; 1 ppm by mass or less of H; and the balance Cu and inevitable impurities, wherein hydrogen concentration after performing a heat treatment at 500&#xb0; for 30 minutes in vacuum is 0.2 ppm by mass or less. The magnet wire includes: a drawn wire material produced by using the copper wire rod; and an insulating film coating an outer periphery of the drawn wire material.

Copper wire rod and magnet wire

Disclosed is a hot rolled plate produced by hot rolling an ingot cast by continuous casting, in which the plate is made of a copper alloy containing 0.5 to 10.0 at % of Ca and the balance consisting of Cu and inevitable impurities and the average grain size of Cu-&#x3b1; phase crystal grains is 5 to 60 &#x3bc;m in a Cu matrix.

Hot rolled plate made of copper alloy used for a sputtering target and sputtering target

A Mn-containing copper alloy sputtering target is provided. The target generates a small number of particles and is used to form diffusion inhibiting films and seed films of interconnects of semiconductor devices simultaneously. The target is a Mn-containing copper alloy sputtering target that generates few particles, comprising a copper alloy containing 0.6 to 30 mass % of Mn with the balance consisting of copper and impurities, wherein the impurities are controlled to include a total of 40 ppm or less of metallic impurities, 10 ppm or less of oxygen, 5 ppm or less of nitrogen, 5 ppm or less of hydrogen, and 10 ppm or less of carbon.

Mn-containing copper alloy sputtering target generating few particles

A method for producing copper alloy materials for molds for continuous steel casting and molds as produced by the method. The molds are highly resistant to thermal fatigue and are hardly cracked. To produce the materials, cast ingots of a copper-based chromium-zirconium alloy comprising from 0.2 to 1.5% by weight of Cr and from 0.02 to 0.2% by weight of Zr are heated at between 900.degree. C. and 1000.degree. C. for 30 minutes or longer and then rolled, while hot, at a reduction ratio of 60% or more to be at 850.degree. C. or higher at which the hot rolling is finished , and immediately after the hot rolling, these are rapidly cooled to 400.degree. C. or lower at a cooling rate of 10.degree.C./sec or more, and then aged at between 400.degree. C. and 520.degree. C. for from 1 hour to 5 hours.