A process and apparatus are described for manufacturing particle stabilized foamed metal slabs. A foam is first formed in a foaming chamber by heating a composite of a metal matrix and finely divided solid stabilizer particles above the solidus temperature of the metal matrix and discharging gas bubbles into the molten metal composite below the surface thereof to thereby form a stabilized liquid foam on the surface of the molten metal composite. The stabilized liquid foam is continuously drawn off the surface of the molten metal composite and is solidified into a shaped foam product while being continuously drawn off.

Process for producing shaped slabs of particle stabilized foamed metal

Shaped articles are produced from foam metal by a procedure wherein the foam is formed by heating a composite of a metal matrix and finely divided solid stabilizer particles above the solidus temperature of the metal matrix and discharging gas bubbles into the molten metal composite below the surface thereof to thereby form a stabilized liquid foam on the surface of the molten metal composite. According to the novel feature the stabilized metal foam in liquid form is shape cast by being pressed into a mould and permitted to cool and solidify. The density of the cast part is essentially unchanged from that of the starting liquid foam.

Process for shape casting of particle stabilized metal foam

A novel lightweight gas metal composite is produced having isolated particle stabilized pores. A composite of a metal matrix, e.g. aluminum, and finely divided solid stabilizer particles, e.g. silicon carbide, is heated above the liquidus temperature of the metal matrix and this is mixed such that a vortex is formed. The molten composite is blanketed with a gas and during the vortex mixing. This gas is drawn into the melt to produce an expanded, viscous molten composite material containing pores which are very small, spherical-shaped and quite evenly distributed. The viscous molten composite material can be directly formed into a solid shaped product and is also capable of being remelted and formed by forming processes without destroying the integrity of the pores. The result is a lightweight expanded metal product capable of being formed into shapes to close dimensional tolerances.

Lightweight metal with isolated pores and its production

A process for coloring a metal surface and colored metal products thus produced. The process involves forming a layer of a metal oxide on a surface of the metal to be colored and then bringing about permanent plastic deformation of the surface. If the oxide layer is of a suitable thickness (e.g. 500.ANG.-1 .mu.m) and the deformation is sufficiently high (preferably producing a reduction in thickness of the metal article by 30% or more), the resulting metal article exhibits an attractive color (usually a dichroic pastel color). The article can then be fabricated into finished articles, e.g. beverage cans, in the usual way.

Process for coloring metal surfaces

A method is described for producing foamed metal in which gaseous bubbles are retained within a mass of molten metal during foaming. The method comprises heating a composite of a metal matrix and finely divided solid stabilizer particles above the liquidus temperature of the metal matrix, discharging gas bubbles into the molten metal composite below the surface thereof to thereby form a foamed melt on the surface of the molten metal composite and cooling the foamed melt thus formed below the solidus temperature of the melt to form a solid foamed metal having a plurality of closed cells. A novel foamed metal product is also described.

Stabilized metal foam body

A method is described for producing foamed metal in which gaseous bubbles are retained within a mass of molten metal during foaming. The method comprises heating a composite of a metal matrix and finely divided solid stabilizer particles above the liquidus temperature of the metal matrix, discharging gas bubbles into the molten metal composite below the surface thereof to thereby form a foamed melt on the surface of the molten metal composite and cooling the foamed melt thus formed below the solidus temperature of the melt to form a solid foamed metal having a plurality of closed cells.