An exemplary embodiment of an aluminum type plated steel sheet which excels in discoloration resistance, and weldability, which does not decorate after re-heating and which can prevent increasing of strength, and a heat shrink band using the same are provided. For example, the heat shrink band can be made of an aluminum type plated steel sheet consisting of a steel sheet being composed of, e.g., not more than about 0.005 mass % of C; not more than about 0.005 mass % of N; not less than about 0.1 mass % and not more than about 0.5 mass % of Si; not more than about 0.1 mass % of P; not more than about 0.02 mass % of S; not less than about 1.05 mass % and not more than 2.0 mass % of Mn; not more than 1.0 mass % of sol Al; a residual amount of Fe and inevitable impurities, and an aluminum type plated layer mainly consisting of Al being deposited thereon. Such exemplary sheet can be prevented from a discoloration upon, e.g., being re-heated at a temperature of not less than about 500&#xb0; C. to not more than about 700&#xb0; C.

Aluminum type plated steel sheet and heat shrink band using the same

The present invention provides a cold-rolled steel sheet and a hot-dip galvanized steel sheet having good bake hardenability, non-aging properties at room temperature and good formability and a process for producing the same. An extra low carbon steel or an extra low carbon steel containing at least one element selected from Ti and Nb is annealed at a temperature of not lower than the AC.sub.3 transformation point to bring the structure after annealing to a structure of low-temperature transformation products. This makes it possible to provide a steel sheet that has a combination of high paint-bake hardenability and non-aging properties at room temperature and is excellent also in formability in respect of average r value (deep drawability) and elongation (punch stretchability). In particular, with respect to paint-bake hardenability, a BH property on a high level up to about 10 kgf/mm.sup.2 can be imparted according to need, and it is possible to provide a cold-rolled steel sheet and a hot-dip galvanized cold-rolled steel sheet that also have a non-aging property at room temperature.

Cold-rolled steel sheet and hot-dip galvanized cold-rolled steel sheet

Non-aging at room temperature ferritic single-phase cold-rolled steel

Cold rolled steel sheet and hot dip zinc-coated cold rolled steel sheet