Coors Container Company

King G Robertson

Donald C McAuliffe

A composition and method whereby aluminum scrap, including consumer scrap, is recycled into aluminum sheet and aluminum containers. Aluminum scrap is melted in a heated furnace to form a melt composition. The melt is adjusted to form the present composition, consisting essentially of silicon, 0.1-1.0%; iron 0.1-0.9%; manganese 0.4-1.0%; magnesium 1.3-2.5%; copper 0.05-0.4%; and titanium, 0-0.2%, the balance being essentially aluminum. Aluminum scrap comprising consumer scrap, plant scrap, and can making scrap is heated to form the melt composition, which requires a minimum amount of adjustment to arrive at the present alloy composition. The composition is then cast and fabricated into sheet having strength and formability properties making it suitable for container manufacture. Container manufacture according to the process and composition of the present invention comprises drawn-and-ironed can body manufacture and easy-opening end manufacture. Sheet fabrication according to the present invention comprises direct chill casting, scalping, preheating, hot breakdown rolling, continuous hot rolling, annealing, cold rolling and shearing. Sheet manufacture may also comprise continuous strip casting and solution heat treatment.

Method of recycling aluminum scrap into sheet material for aluminum

A composition and method whereby aluminum scrap, including consumer scrap, is recycled and fabricated into aluminum sheet and aluminum containers. Aluminum scrap is melted in a heated furnace to form a melt composition. The melt is adjusted to form the present composition, consisting essentially of silicon, 0.1-1.0%; iron 0.1-0.9%; manganese 0.4-1.0%; magnesium 1.3-2.5%; copper 0.05-0.4%; and titanium, 0-0.2%, the balance being essentially aluminum. Aluminum scrap comprising consumer scrap, plant scrap, and can making scrap is heated to form the melt composition, which requires a minimum amount of adjustment to arrive at the present alloy composition. The composition is then cast and fabricated into sheet having strength and formability properties making it suitable for container manufacture. Container manufacture according to the process and composition of the present invention comprises drawn-and-ironed can body manufacture and easy-opening end manufacture. Sheet fabrication according to the present invention comprises direct chill casting, scalping, preheating, hot breakdown rolling, continuous hot rolling, annealing, cold rolling and shearing.

Fabrication of aluminum alloy sheet from scrap aluminum for container

A composition whereby aluminum scrap, including consumer scrap, is recycled into aluminum sheet and aluminum containers. Aluminum scrap is melted in a heated furnace to form a melt composition. The melt is adjusted to form the present composition, consisting essentially of silicon, 0.1-1.0%; iron 0.1-0.9%; manganese 0.4-1.0%; magnesium 1.3-2.5%; copper 0.05-0.4%; and titanium, 0-0.2%, the balance being essentially aluminum. Aluminum scrap comprising consumer scrap, plant scrap, and can making scrap is heated to form the melt composition, which requires a minimum amount of adjustment to arrive at the present alloy composition. The composition is suitable for fabrication into sheet having strength and formability properties making it suitable for container manufacture. Container manufacture according to the process and composition of the present invention comprises drawn-and-ironed can body manufacture and easy-opening end manufacture. Sheet fabrication according to the present invention comprises conventional direct chill casting or continuous strip casting.

Growing community of inventors

Golden, CO, United States of America

King G Robertson