A method for preparing a carbide protective layer comprises: (A) mixing a carbide powder, an organic binder, an organic solvent and a sintering aid to form a slurry; (B) spraying the slurry on a surface of a graphite component to form a composite component; (C) subjecting the composite component to a cold isostatic pressing densification process; (D) subjecting the composite component to a constant temperature heat treatment; (E) repeating steps (B)-(D) until a coating is formed on a surface of the composite component; (F) subjecting the coating to a segmented sintering process; (G) obtaining a carbide protective layer used for the surface of the composite component. Accordingly, while the carbide protective layer can be completed by using the wet cold isostatic pressing densification process and the cyclic multiple superimposition method, so that it can improve the corrosion resistance in the silicon carbide crystal growth process environment.

Method for preparing carbide protective layer

A method for the formation of tantalum carbides on a graphite substrate includes the steps of: (a) adding an organic tantalum compound, a chelating agent, a pre-polymer to an organic solvent to form a tantalum polymeric solution; (b) subjecting a graphite substrate with the tantalum polymeric solution to a curing process to form a polymeric tantalum film on the graphite substrate; and (c) subjecting the polymeric tantalum film on the graphite substrate in an oven to a pyrolytic reaction in the presence of a protective gas to obtain a protective tantalum carbide on the graphite substrate.

Method for the formation of tantalum carbides on graphite substrate

A method for fabricating an ultra-thin graphite film on a silicon carbide substrate includes the steps of: (A) providing a polyamic acid solution and a siloxane-containing coupling agent for polymerizing under an inert gas atmosphere to form a siloxane-coupling-group-containing polyamic acid solution; (B) performing a curing process after applying the siloxane-coupling-group-containing polyamic acid solution to a silicon carbide substrate; (C) placing the silicon carbide substrate in a graphite crucible before placing the graphite crucible in a reaction furnace to perform a carbonization process under an inert gas atmosphere; (D) subjecting the silicon carbide substrate to a graphitization process to obtain a graphite film, thereby make it possible to fabricate an ultra-thin graphite film of high-quality on the surface of silicon carbide in a lower graphitization temperature range.

Method for fabricating ultra-thin graphite film on silicon carbide substrate from siloxane-coupling-group-containing polyamic acid solution