The invention relates to a thin metal sheet which is made of an alloy based on substantially recrystallized aluminum and which has a thickness of 0.25 to 12 mm, the alloy comprising, in percent by weight, Cu 3.4-4.0; Mg 0.5-0.8; Mn 0.1-0.7; Fe #0.15; Si #0.15; Zr #0.04; Ag #0.65; Zn #0.5; inevitable impurities #0.05 each and #0.15 in total, the remainder consisting of aluminum. The invention also relates to a process for manufacturing such a metal sheet and to the use thereof as a fuselage panel or sheet metal for the production of composite products such as fiber metal laminates (FML) for wing or fuselage applications in the aeronautical industry.

Metal sheet made of high-strength 2XXX alloy for an aircraft fuselage

The invention relates to a product made of an aluminium-based alloy comprising, by wt. %, Cu: 2.4-3.2; Li: 1.6-2.3; Mg: 0.3-0.9; Mn: 0.2-0.6; Zr: 0.12-0.18; such that Zr&#x2265;&#x2212;0.06 *Li+0.242; Zn: &#x3c;1.0; Ag: &#x3c;0.15; Fe+Si&#x2264;0.20; optionally, at least one element selected from Ti, Sc, Cr, Hf and V, the content of the element, if selected, being: Ti: 0.01-0.1; Sc: 0.01-0.15; Cr: 0.01-0.3; Hf: 0.01-0.5; V: 0.01-0.3; other elements &#x2264;0.05 each and &#x2264;0.15 in total; the remainder being aluminium. The invention also relates to a method for manufacturing an as-cast aluminum alloy product according to the invention, comprising the following steps: preparing a liquid metal bath; casting an as-cast shape from said liquid metal bath; and solidifying the as-cast shape into a billet, a rolling plate or a forging blank; characterised in that the casting is performed without adding any grain refiner, or by adding a refiner comprising (i) Ti and (ii) B or C, such that the content of B from the refiner is less than 45 ppm, and that of C is less than 6 ppm, and/or characterised in that the casting is carried out, for an as-cast shape of thickness E or with a diameter D greater than 150 mm, at a casting rate v (mm/min) greater than 30 for a plate-type as-cast shape or 9000/D for a billet-type as-cast shape.

Low-density aluminum-copper-lithium alloy products

The invention relates to a plate with a thickness of 0.5 to 9 mm with an essentially recrystallized granular structure, made from an alloy based on aluminum, comprising 2.8 to 3.2% by weight Cu, 0.5 to 0.8% by weight Li, 0.1 to 0.3% by weight Ag, 0.2 to 0.7% by weight Mg, 0.2 to 0.6% by weight Mn, 0.01 to 0.15% by weight Ti, a quantity of Zn below 0.2% by weight, a quantity of Fe and Si of less than or equal to 0.1% by weight each, and unavoidable impurities to a proportion of less than or equal to 0.05% by weight each and 0.15% by weight in total, said plate being obtained by a method comprising casting, homogenization, hot rolling and optionally cold rolling, solution heat treatment, quenching and aging. The plates according to the invention are advantageous in particular for the manufacture of aircraft fuselage panels.

Isotropic plates made from aluminum-copper-lithium alloy for manufacturing aircraft fuselages

The invention relates to a method for manufacturing a thin sheet having a thickness of 0.5 to 3.3 mm and an essentially non-recrystallized structure made of aluminum-based alloy.

Thin sheets made of an aluminium-copper-lithium alloy for producing airplane fuselages