A nitrided steel product or thin cast steel strip comprising, by weight, less than 0.25% carbon, between 0.20 and 2.0% manganese, between 0.05 and 0.50% silicon, less than 0.01% aluminum, niobium between 0.01 and about 0.20%, and between 0.01 and 0.075% nitrogen, and having a majority of the microstructure comprised of bainite and acicular ferrite, having more than 70% niobium in solid solution prior to nitriding and having yield strength between 650 MPa and 800 MPa and tensile strength between 750 MPa and 900 MPa.

Nitriding of niobium steel and product made thereby

A steel product or thin steel cast strip including, by weight, less than 0.25% carbon, between 0.20 and 2.0% manganese, between 0.05 and 0.50% silicon, less than 0.01% aluminum, and at least one of niobium between 0.01% and 0.20% and vanadium between 0.01% and 0.20%, and a microstructure of a majority bainite and acicular ferrite, and more than 70% niobium and/or vanadium in solid solution. The steel product may have an increase in elongation and an increase in yield strength after age hardening. The age hardened steel product may have niobium carbonitride particles with an average particle size of 10 nanometers and less, and may have substantially no niobium carbonitride particles greater than 50 nanometers. The steel product may have a yield strength of at least 380 MPa, a tensile strength of at least 410 MPa, or both. The product may have a total elongation of at least 6% or 10%.

High strength thin cast strip product and method for making the same

A steel product having, by weight, less than 0.25% carbon, between 0.20 and 2.0% manganese, between 0.05 and 0.50% silicon, aluminum 0.008% or less by weight, and at least one element selected from the group consisting of titanium between about 0.01% and about 0.20%, niobium between about 0.01% and about 0.20%, molybdenum between about 0.05% and about 0.50%, and vanadium between about 0.01% and about 0.20%, and having a microstructure comprised of a majority bainite, and fine oxide particles of silicon and iron distributed through the steel microstructure of average precipitate size less than 50 nanometers. The yield strength of the steel product may be at least 55 ksi (380 MPa) or the tensile strength of at least 500 MPa, or both. The steel product may have total elongation of at least 6% or 10%, and thickness less than 3.0 mm.

Thin cast strip product with microalloy additions, and method for making the same

A method of producing coil plate on a hot strip mill is disclosed. The method includes coiling hot rolled coil plate strip at a temperature that is selected (a) to minimize precipitation of Cr/Mo carbides or (b) so that any Cr/Mo carbides that form are sufficiently fine that they go into solution in any subsequent heat treatment of coil plate made from the strip.

Linepipe steel

A steel product or thin steel cast strip comprised of, by weight, less than 0.25% carbon, between 0.20 and 2.0% manganese, between 0.05 and 0.50% silicon, less than 0.01% aluminum, and at least one of niobium between 0.01% and 0.20% and vanadium between 0.01% and 0.20%, and having a microstructure of a majority bainite and acicular ferrite, and more than 70% niobium and/or vanadium in solid solution. The steel product may have an increase in elongation and an increase in yield strength after age hardening. The age hardened steel product may have niobium carbonitride particles with an average particle size of 10 nanometers and less, and may have substantially no niobium carbonitride particles greater than 50 nanometers. The steel product may have a yield strength of at least 380 MPa or a tensile strength of at least 410 MPa, or both. The steel product or thin cast steel strip may have a total elongation of at least 6% or 10%.

A steel product with a high austenite grain coarsening temperature having less than 0.4% carbon, less than 0.06% aluminium, less than 0.01% titanium, less than 0.01% niobium, and less than 0.02% vanadium by weight, and having fine oxide particles containing silicon and iron distributed through the steel microstructure having an average particle size less than 50 nanometers and may be between 5 and 30 nanometers. The steel product may have fine oxide particles distributed through the microstructure capable of restricting ferrite recrystallization for strain levels up to at least 10.0%, for temperatures up to 750&#xb0; C. with holding times up to 20 minutes. The steel product may be made by continuous casting of steel strip introduced between the casting rolls to form a casting pool of molten carbon steel having a total oxygen content of at least 70 ppm usually less than 250 ppm, and a free oxygen content 20 and 60 ppm, counter rotating the casting rolls.

Steel product with a high austenite grain coarsening temperature

A steel product with a high austenite grain coarsening temperature having less than 0.4% carbon, less than 0.06% aluminium, less than 0.01% titanium, less than 0.01% niobium, and less than 0.02% vanadium by weight, and having fine oxide particles containing silicon and iron distributed through the steel microstructure having an average particle size less than 50 nanometers and may be between 5 and 30 nanometers. The steel product may have fine oxide particles distributed through the microstructure capable of restricting ferrite recrystallisation for strain levels up to at least 10.0%, for temperatures up to 750&#xb0; C. with holding times up to 20 minutes. The steel product may be made by continuous casting of steel strip introduced between the casting rolls to form a casting pool of molten carbon steel having a total oxygen content of at least 70 ppm usually less than 250 ppm, and a free oxygen content 20 and 60 ppm, counter rotating the casting rolls.