Maumee Research & Engineering, Incorporated

James Alan Thornton

Franklin G Rinker

Deane Avent Horne

Valdis R Daiga

A rotary hearth furnace for reducing a feed material is disclosed. The rotary hearth furnace includes a rotating hearth disposed in an enclosure and mounted for rotary movement. The enclosure includes an annular inner wall, an annular outer wall and a roof. The enclosure is sealed to the hearth and divided into a plurality of zones including at least a loading zone, a process zone and a discharge zone. The furnace further includes a plurality of burners positioned in at least the outer wall of the enclosure to provide a controlled temperature within the rotary hearth furnace and a flue positioned within the reduction zone of the furnace between the preheat zone and the discharge zone to exhaust combustion gases from the burners and gases resulting from the processing of the feed material. Said flue contains space for combustion and settling of the unburned particulates. A water spray quench reduces the temperature of the furnace off-gas so that subsequent combustion by the introduction of air or oxygen does not produce significant nitrogen oxides.

Method and apparatus for reducing a feed material in a rotary hearth furnace

A process for recovering iron from iron-bearing materials including steel mill waste and iron-bearing ores. The process includes the steps of providing a mixture of iron-bearing materials having iron oxides therein and carbonaceous material. Blending with the mixture an organic binder. The mixture is then agglomerated to form green compacts. The green compacts are then loaded into a preheated rotary hearth furnace void of compacts to form a layer of compacts no more than about two compacts high. The green compacts are heated for about 5-12 minutes at a temperature of between about 2200-2500&deg; F. to reduce the compacts and evolve undesirable oxides from the compacts. The reduced compacts are then discharged from the rotary hearth furnace whereupon they are soaked to provide additional time for reaction to achieve 99% or more reduction of the iron oxides. The metallized iron compacts may then be cooled or transported hot to a steel making operation.

Process for treating metal oxide fines

A process for treating iron-bearing material with a carbonaceous material to form a mixture, wherein the amount of carbonaceous material added exceeds the stoichiometric amount required to reduce the metal oxide to elemental metal. In one embodiment, the process also includes blending an organic binder with the mixture. The mixture is agglomerated using compaction to bond the mixture and form green compacts. The green compacts are loaded into a heated furnace and heated for about 5-12 minutes at a temperature of between about 2100.degree.-2500.degree. F. and at a CO/CO.sub.2 ratio of about 1.5-2.5 proximate the discharge area to reduce the iron oxide containing compacts to compacts containing elemental iron and an excess amount of carbonaceous material wherein the excess amount of carbonaceous material counteracts re-oxidation of the elemental iron. The reduced compacts are then discharged from the furnace. The furnace includes counterflow and co-flow exhaust to maintain the charge area and the discharge area of the furnace at a pressure about equal to atmospheric pressure.

Process for treating iron bearing material

A process for recovering iron from iron-bearing materials including steel mill waste and iron-bearing ores. The process includes the steps of providing a mixture of iron-bearing materials having iron oxides therein and carbonaceous material. The mixture is agglomerated to form green compacts. The green compacts are then loaded into a preheated rotary hearth furnace void of compacts to form a layer of compacts no more than about two compacts high. The green compacts are heated for about 5 to 12 minutes at a temperature of between about 2200.degree. F. to 2500.degree. F. to reduce the compacts and evolve undesirable oxides from the compacts. The reduced compacts are then discharged from the rotary hearth furnace whereupon they are soaked to provide additional time for reaction to achieve 99% or more reduction of the iron oxides. The metallized iron compacts may then be cooled or transported hot to a steel making operation.