A heat-resistant nickel-based alloy having excellent welding properties, said nickel-based alloy consisting essentially of, in terms of wt. %, 0.05 to 0.25% of C, 18 to 25% of Cr, 15 to 25% of Co, at least one selected from the group consisting of up to 3.5% of Mo and 5 to 10% of W, with W+1/2Mo being 5 to 10%, 1.0 to 5.0% of Ti, 1.0 to 4.0% of Al, 0.5 to 4.5% of Ta, 0.2 to 3.0% of Nb, 0.005 to 0.10% of Zr, 0.001 to 0.01% of B and the balance being Ni and unavoidable impurities, wherein the (Al+Ti) content and the (W+1/2Mo) content are within the range surrounded by the lines connecting points A (Al+Ti: 5%, W+1/2Mo: 10%), B (Al+Ti: 5%, W+1/2Mo: 5%), C (Al+Ti: 7%, W+1/2Mo: 5%), and D (Al+Ti: 7%, W+1/2Mo: 10%) excluding the line A-B in FIG. 1. Another alloy has substantially the same composition as described above except that the Cr content is 10 to 20% and the (Al+Ti) content and the (W+1/2Mo) content are within the range surrounded by the lines connecting points A, B, E (Al+Ti: 4%, W+1/2Mo: 5%), F (Al+Ti: 4%, W+1/2Mo: 0.5%), G (Al+Ti: 7%, W+1/2Mo: 0.5%) and D, excluding the line A-B-E, in FIG. 1.

Heat-resistant nickel-based alloy excellent in weldability

A rotating blade or stationary vane of a gas turbine which is made of a nickel alloy containing Cr, Co, Mo, W, Ta, Al, Ti, C, B, Zr, and one or both of Mg and Ca. Additionally, the alloy may contain Hf, Pt, Rh and Re.

Rotating blade or stationary vane of a gas turbine

The improved nickel-base heat-resistant alloy consists of 13.1-15.0% Cr (all percentages that follows are by weight), 8.5-10.5% Co, 1.0-3.5% Mo, 3.5-4.5% W, 3.0-5.5% Ta, 3.5-4.5% Al, 2.2-3.2% Ti, 0.06-0.12% C, 0.005-0.025% B, 0.010-0.05% Zr and 1-100 ppm of Mg and/or Ca, in the optional presence of 0-1.5% Hf and/or 0-0.5% of at least one element of Pt, Rh and Re, with the remainder being Ni and incidental impurities. The alloy has high strength and high resistance to oxidation and corrosion at elevated temperatures and, hence, is suitable for use as a constituent material for machine parts that are to be exposed to elevated temperatures.

Nickel-base heat-resistant alloys

A heat resistant nickel base alloy which is excellent in not only hot and cold workability but also high temperature strength properties and which also possesses satisfactory oxidation resistance. The nickel base alloy consists essentially of 0.001-0.15 percent carbon, 0.0005-0.05 percent calcium, 20.0-126.0 percent chromium, 4.7-9.4 percent cobalt, 5.0-16.0 percent molybdenum, 0.5-4.0 percent tungsten, with the total of molybdenum plus tungsten being from 9.0 to 16.5 percent, and the balance nickel and inevitable impurities. The alloy may further contain one selected from the group consisting of (1) 0.3-1.5 percent aluminum and 0.1-1.0 percent titanium, (2) 0.001-0.30 percent at least one of yttrium and rare earth elements, and (3) 0.01-1.0 percent at least one of niobium, vanadium and tantalum, whereby the aforementioned characteristics are further enhanced.

Heat resistant nickel base alloy excellent in workability and high