A polishing pad contains: a polishing layer having a polishing surface for polishing a workpiece; and a cushion layer disposed on the side of the polishing layer opposite from the polishing surface. With regard to the ratio (tan δ) of the storage elastic modulus E' to the loss elastic modulus E″ of the whole polishing pad, as obtained through dynamic viscoelasticity measurement using frequency dispersion (25° C.) in a bending mode, the ratio of the maximum value of tan δ measured at 100-1000 rad/s (tan δ) to the maximum value of tan δ measured at 1 to 10 rad/s (tan δ) is 0.75 to 1.30.

Polishing pad

A polishing pad is equipped with a polishing layer having a polyurethane sheet, wherein a tan δ peak value change rate determined by formula: tan δ peak value change rate=|tan δ peak−tan δ peak|/tan δ peak×100, is not more than 15%, where tan δ peakrepresents the peak value of the loss tangent tan δ, of the polyurethane sheet in a wet state after being immersed in water for three days, within a temperature range of 20-100° C. in a tensile mode under an initial load of 148 g with a strain range of 0.1% at a measurement frequency of 1.6 Hz, and tan δ peakrepresents the peak value of the loss tangent tan δ, of the polyurethane sheet in a dry state without being immersed in water, within a temperature range of 20-100° C. in a tensile mode under an initial load of 148 g with a strain range of 0.1% at a measurement frequency of 1.6 Hz.

Polishing pad and method for manufacturing same

A polishing pad includes: a polishing layer having a polyurethane sheet containing substantially spherical cells, wherein E'(90%)/E&#x2032;(30%) falls within a range of 0.4 to 0.7, where E&#x2032;(90%) represents a storage modulus of the polyurethane sheet that has been exposed to an environment with a temperature of 23&#xb0; C. and a relative humidity of 90%, as measured in a tension mode at 40&#xb0; C. with an initial load of 148 g, a strain range of 0.1%, and a measurement frequency of 1.6 Hz, and E&#x2032;(30%) represents a storage modulus of the polyurethane sheet that has been exposed to an environment with a temperature of 23&#xb0; C. and a relative humidity of 30%, as measured in a tension mode at 40&#xb0; C. with an initial load of 148 g, a strain range of 0.1%, and a measurement frequency of 1.6 Hz. Also provided is a method for manufacturing the polishing pad.

A lapping material having a knitted fabric constituted by warp knitting or weft knitting, and a resin with which the knitted fabric is impregnated.

Lapping material and method for producing the same, and method for producing polished product