A process for hardening aluminum comprises the steps of adding a magnesium hardener to molten aluminum wherein the hardener has a magnesium content in the range of 64-72 wt % based on the weight of the hardener, with a remaining portion of the hardener comprising aluminum. The process may further include the steps of preheating the hardener prior to adding the hardener to the aluminum for decreasing a temperature differential between the hardener and the aluminum so as to stabilize the hardener and prevent shattering thereof.

Process for hardening aluminum using a magnesium alloy

A process for producing a magnesium alloy aluminum hardener comprises the steps of providing magnesium alloy scrap, wherein the scrap comprises aluminum present in a range of 1-10 wt. % based on the weight of the scrap and at least one of zinc present in a range of 0.1-3 wt. % based on the weight of the scrap and manganese present in a range of 0.1-3 wt. % based on the weight of the scrap, wherein a remaining portion of the scrap comprises magnesium; providing molten aluminum; and adding the scrap to the molten aluminum until the hardener is produced having a magnesium content in a range of 64-72 wt. % based on the weight of the hardener, with a remaining portion of the hardener comprising aluminum and at least one of zinc and manganese.

Magnesium alloy as an aluminum hardener

Aluminum base alloy consisting essentially of from 0.1 to 3.0% boron, from 1 to 10% titanium and the balance essentially aluminum wherein the aluminum matrix contains TiB.sub.2 particles dispersed throughout said matrix having an average particle size of less than 1 micron, and wherein the matrix contains clusters of said TiB.sub.2 particles greater than 10 microns in size with an average of less than 4 of said clusters per 2 cm.sup.2. The alloy is prepared by adding a boron containing material selected from the group consisting of borax, boron oxide, boric acid and mixtures thereof, and K.sub.2 TiF.sub.6 to a bath of molten aluminum and stirring the molten mixture.

Aluminum base alloy

Aluminum base alloy and method for preparing same