Macmillan Bloedel Limited

David M Mackie

Peter Joyce

A two-stage chemical treatment process is disclosed for increasing the density, strength and brightness properties of mechanical wood pulp. The method comprises the steps of: applying an aqueous solution of sodium sulfite in the range of about 1%-10% sodium sulfite based on bone dry weight of wood to wood particles, the solution having a pH in the range of about 4.5-11; heating the sodium sulfite treated wood particles to a temperature in the range of about 100.degree.-160.degree. C. and maintaining the particles in the temperature range for a period of time in the range of about 20 seconds to 10 minutes; refining the heated sodium sulfite treated wood particles into mechanical wood pulp; separating the pulp into a reject fraction and an accept fraction, the reject fraction containing a higher proportion of shives and long fiber material; applying an aqueous solution of sodium sulfite, in the range of about 4%-50% sodium sulfite based on bone dry weight of wood, to the reject fraction, the solution having a pH in the range of about 4.5-11; cooking the sodium sulfite treated reject fraction at a temperature in the range of about 100.degree.-160.degree. C. for a period of time in the range of about 2-120 minutes; refining the cooked sodium sulfite treated reject fraction; and recombining at least part of the refined reject fraction with at least part of the accept fraction.

Two-stage chemical treatment of mechanical wood pulp with sodium sulfite

A method is described for increasing the yield of pulp obtained from an alkaline pulping process. A lignocellulosic material, such as wood chips, is first pretreated with an aqueous solution containing from 0.1 to 10% by weight of monoethanolamine, methylamine or dimethylamine and from 0.01 to 1% by weight of copper sulfate or nickel sulfate at elevated temperature and pressure in a closed vessel. This pretreated material is then subjected to conventional alkaline pulping, preferably soda or two-stage soda-oxygen pulping.

Alkaline pulping of lignocellulosic material with amine and sulfate

A method is described for increasing the yield of pulp obtained from an alkaline pulping process. A lignocellulosic material, such as wood chips, is first pretreated with an aqueous solution containing from 0.1 to 10% by weight of monoethanolamine, methylamine or dimethylamine and from 0.01 to 1% by weight of copper nitrate or nickel nitrate at elevated temperature and pressure in a closed vessel. This pretreated material is then subjected to conventional alkaline pulping, preferably soda or two-stage soda-oxygen pulping.

Growing community of inventors

Vancouver, Canada

David M Mackie