A nickel-base alloy suitable for overlaying steel substrates. The alloy and steel have similar thermal conductivities and thermal coefficients of expansion. The alloy broadly initially contains about 15-20% molybdenum, about 5-10% chromium, up to about 2% iron, up to about 5% tungsten and/or niobium, up to about 0.1% carbon, and the balance essentially nickel.

Alloy overlay having thermal characteristics similar to those of a

The invention provides a welding material for welding iron containing low CTE alloys. The filler metal contains 25-55% nickel, 0-30% cobalt, 0.05-0.5% carbon, 0.25-5% niobium and balance iron with incidental impurities. The welding material also is operable with fluxes for submerged arc welding. In addition, the welding material may be configured to function as a flux coated or flux-cored electrode.

Welding material for low coefficient of thermal expansion alloys

The invention provides a method of improving cleaning operations for metals. A fluorescent dye is introduced into metal treatment solution and the surface of a metal product is treated with the treatment solution. The metal product with the treatment solution on its surface is worked to deform the metal product. The treatment solution is removed from the surface of the metal product to clean the metal product. The cleaned metal product is illuminated with excitation energy capable of stimulating fluorescence in the fluorescent dye. Fluorescence of the fluorescent dye is optically monitored to determine effectiveness of the removing step.

Method of monitoring removal of metal treatment solutions

A material for electric heater element sheathing, which has good weldability, is oxidation- and corrosion-resistant, and forms an eye-pleasing dark gray or black surface oxide, consists essentially of, by weight, from about 8.75-15.5% nickel, about 19.5-21.0% chromium, about 0.30-0.50 manganese, about 0.50-2.0% silicon, about 0.25-0.60% aluminum, about 0.25-1.0% titanium, up to about 0.05% carbon, up to about 0.005% sulfur, up to about 0.75% copper, up to about 1.0% cobalt, up to about 1.0% molybdenum, up to about 0.02% phosphorus, about 0.001-0.015% calcium plus magnesium and remainder essentially iron, wherein the Ferrite Number is between 1 and 15.

Heater sheath alloy

The invention provides a welding electrode useful for reducing nitrogen porosity in a weld. A metallic base having 1.5 to 6 weight percent titanium, balance essentially nickel is used. The resulting deposit has less than 0.5 weight percent titanium to ensure close match of tolerances. A flux is used in combination with the metallic base to control arc behavior, atmosphere content and slag characteristics.

Low porosity welding electrode

A material for electric heater element sheathing, which has good weldability, is oxidation- and corrosion-resistant, and forms an eye-pleasing dark gray or black surface oxide, consists essentially of, by weight, from about 8.75-15.5% nickel, about 19.5-21.0% chromium, about 0.30-0.50 manganese, about 0.50-2.0% silicon, about 0.25-0.60% aluminum, about 0.25-1.0% titanium, up to about 0.05% carbon, up to about 0.005% sulfur, up to about 0.75% copper, up to about 1.0% cobalt, up to about 1.0% molybdenum, up to about 0.02% phosphorus, about 0.001-0.015% calcium plus magnesium and remainder essentially iron, wherein the Ferrite Number is between 3 and 15.

The invention provides a coated electrode suitable for welding stainless steel. The coated electrode uses a stainless steel core wire. The flux contains by weight percent a total of 0 to 14.5 alkali metal and aluminum fluoride, about 0.5 to 12.5 cerium fluoride, a total of about 10 to 30 alkali metal and manganese carbonate, about 2 to 25 cerium oxide plus zirconium, about 0 to 25 chromium, about 0 to 10 manganese, about 5 to 15 total metal fluorides, and balance rutile. A binder holds the flux to the stainless steel core.