An apparatus and method for drawing low loss fluoride glass fibers from a preform. A stream of reactive gas is passed around the preform and fiber so as to prevent moisture and oxygen contamination of the fiber while the fiber is being drawn. The apparatus includes an insulating vessel which surrounds a heating chamber in which the fiber is drawn, and a very narrow heating zone within the chamber for preventing crystallization of the drawn fiber.

Apparatus and method for drawing glass fibers

A biocompatible optical fiber tip derived from fluorophosphate glasses whose composition includes P--O compounds, AlF.sub.3, alkali-earth fluorides, and/or alkali fluorides, and lanthanides fluoride is used with a medical laser to transmit power for surgical applications.

Biocompatible optical fiber tip for in vivo laser surgery

An improved optical glass fiber for transmitting mid infrared wavelength laser light in surgical instruments, includes a heavy-metal oxide component, preferably GeO.sub.2 doped with heavier cations and anions, and which is capable of delivering at least three watts of laser power continuously for more than ten minutes, without failure. This glass fiber has an .alpha.(dB/m) at 2.94 .mu.m of 10, preferably less, and can transmit at least 27% of the IR through a thickness of one foot.

Heavy metal-oxide glass optical fibers for use in laser medical surgery

An improved optical fiber for transmitting mid-infrared wavelength laser light in surgical instruments, includes, a heavy-metal oxide component, preferably GeO.sub.2 doped with heavier cations and anions, is capable of delivering of at least three watts of laser power continuously for more than ten minutes, without failure. This glass fiber has an .alpha.(dB/m) at 2.94.mu.m of 10, preferably less, and can transmit at least 27% of the IR through a thickness of one foot.

A method for fabricating defect-free optical fiber preforms without light scattering defects such as core-clad interface bubbles, core-clad crystalline inclusions and core glass crystals involves first forming a cladding glass shell preferably by rotational casting, then separately melting core glass inside a cylindrical crucible and quenching using metallic quenching blocks to prevent crystal formation in the core glass, next heating the core containing crucible to the core glass softening point and also heating the cladding tube containing mold to the glass transition temperature of the cladding glass, then placing the cladding tube containing mold inside the core glass crucible and pushing it downwardly with high pressure so that the softened core glass is forced into the cladding glass tube, and finally the preform is annealed to remove thermal stress. Subsequently, the preform is drawn into optical fibers using conventional technology.

Method for making optical fiber preforms

Improved fluoride glass optical fibers are produced by a process introducing several improvements in the production of fluoride glass preforms and the drawing of fibers therefrom. Reduced bubble formation and crystallization are obtained by vertically spinning a fluoride glass melt within a glass cladding tube at a high rotational speed, or alternatively, pouring a flouride glass core melt into a cladding tube while slowly raising the mold from an inclined position to a vertical position, or alternatively, introducing a core tube inside a cladding tube. The production of fibers is enhanced if at least one production phase, i.e., preform formation or fiber drawing, is conducted in an atmosphere containing reactive gases that scavenge molecules that could otherwise react with, hydrolyze and oxidize the fluoride glass. The disclosure also describes several devices uniquely useful in the process of the present invention. In another aspect of the present invention, fluoride glass fibers may be clad with a fluoropolymer which is coated with a polymerizable resin.

Fluoride glass fibers with reduced defects

A process for producing high quality optical glass from fluoride glasses comprising preparing a melt of the glass and then cooling the melt in-situ inside the melt crucible. The in-situ quenching technique can be improved by narrowing the temperature range between the liquidus temperature and the glass transition temperature of the glass. The stability of the fluoride glass can be increased and the liquidus temperature of the glass can be lowered by doping the glass with a chloride dopant. Thorium tetrafluoride can be added to the chloride-doped glass in order to increase the chemical stability of the glass.

In-situ quenched fluoride glasses

A novel solution of H.sub.3 BO.sub.3 dissolved in strong hydrochloric or nitric acid is used to etch fluoride glass preforms used to manufacture fluoride glass fibers. Because of the excellent cleaning ability of the present solution, as well as the absence of sub-micron deposits, the resulting fibers have excellent bending strength.

High-strength fluoride glass fibers and process of making

This invention relates to the immobilization of toxic, e.g., radioactive materials, internally in a silicate glass or silica gel matrix for extremely long periods of time. Toxic materials, such as radioactive wastes containing radioactive anions, and in some cases cations, which may be in the form of liquids, or solids dissolved or dispersed in liquids or gases, are internally incorporated into a glass matrix, having hydrous organofunctionalsiloxy groups, e.g., hydrous aminoalkylsiloxy or carboxyorganosiloxy, bonded to silicon atoms of said glass and/or hydrous polyvalent metals bonded to silicon atoms of said glass through divalent oxygen linkages or otherwise immobilized therein, by a process which involves the ion exchange of said toxic, radioactive anions with hydroxyl groups attached to said organofunctionalsiloxy groups or with hydroxyl groups attached to the hydrous polyvalent metal. Thereafter, the resulting glass now characterized by a distribution of internally bonded or immobilized, toxic, radioactive anions can be packaged in suitable containers, and disposed of as by burial, and/or they can be sintered to collapse the pores thereof to disposal or for producing useful radiation sources. The porous glass or a porous silica gel having said silicon-bonded organofunctionalsiloxy groups and/or said hydrous polyvalent metal oxy groups, the pores of said glass or silica gel remaining open and uncollapsed, can be used advantageously as a backfill for an underground radioactive waste burial site and as overpack in the waste disposal container. Also included is a novel method for bonding the polyvalent metal to the porous silica glass or gel by substituting the protons of the silicon-bonded hydroxyl groups thereof with an alkali metal or ammonium cation followed by displacement of said cation with the non-radioactive polyvalent metal cation.

Fixation by anion exchange of toxic materials in a glass matrix

A method of making fluoride glasses produces fluoride glass having such low OH and low oxide content that the extrinsic optical absorbance caused by the OH vibration at 2.9.mu. is eliminated or substantially reduced. In the method, a glass charge is placed in a capped crucible and dry argon gas is caused to flow through the capped crucible while the temperature is raised to melt the charge. Thereafter, while the dry argon gas flow is continued, the temperature in the furnace is held constant for a time sufficient to obtain a homogenous melt in which all crystalline materials are dissolved. The temperature is then lowered to a value between the glass crystalization temperature and the sublimation temperature of ZrF.sub.4 and then, at isothermal conditions, the flow of dry argon gas is replaced by a flow of SF.sub.6 gas or by a flow of CF.sub.4 gas. At the lowered temperature, the SF.sub.6 or CF.sub.4 gas flow is maintained for a time sufficient to eliminate or greatly reduce OH and oxides in the glass melt. Thereafter, the melt is allowed to cool in a still water-free environment.

SF.sub.6 Process for dehydration of fluoride glasses

This invention relates to the immobilization of toxic materials, e.g., radioactive materials, in glass for extremely long periods of time. Toxic materials, such as radioactive wastes, which may be in the form of liquids, or solids dissolved or dispersed in liquids or gases, are deposited in a glass container which is heated to evaporate off non-radioactive volatile materials, if present; to decompose salts, such as nitrates, if any, and to drive off volatile non-radioactive decomposition products, and then to collapse the walls of said container on said radwaste and seal the container and immobilize the contained radwaste, and then burying the resulting product underground or at sea. In another embodiment, the glass container also contains glass particles, e.g., spheres or granules, on which the radwaste solids are deposited. In other embodiments, the glass container can be made of porous glass or non-porous glass, and/or the contained glass particles can be made of porous or non-porous glass or mixtures of porous or non-porous glass, and/or the glass container can be open at one end and closed at the other or open at both ends, and/or the glass container can be closed at one end with a porous or non-porous closure and open at the other end or closed at the other end with a porous closure. When a porous glass container and/or porous glass particles are used, the radwaste deposits within the pores of the glass which are closed during the subsequent heating step after non-radioactive volatiles have been driven off and prior to sealing the container. There results a substantially impervious glass article in which the radwaste is entrapped and which is highly resistant to leaching action. The products resulting from the use of porous glass, as the container, contents, or both, can be used as sources of radioactivity for a variety of applications in medicine, sterilization, food preservation and any other application where radiation can be beneficially employed.

Immobilization of radwastes in glass containers and products formed

Fluoride glass cladded optical fibers are produced by rotationally casting a fluoride glass cladding tube, introducing core glass melt therein to form a preform, and drawing the preform into a fiber. Disclosed are methods whereby the process may be adopted to the production of multimode, stepped index profile waveguides, single mode waveguides, and waveguides having parabolic index profiles.

Optical fibers having a fluoride glass cladding and method of making

This invention relates to the immobilization of toxic, e.g., radioactive materials, internally in a silicate glass or silica gel matrix for extremely long periods of time. Toxic materials, such as radioactive wastes containing radioactive anions, and in some cases cations, which may be in the form of liquids, or solids dissolved or dispersed in liquids or gases, are internally incorporated into a glass matrix, having hydrous organofunctionalsiloxy groups, e.g., hydrous aminoalkylsiloxy or carboxyorganosiloxy, bonded to silicon atoms of said glass and/or hydrous polyvalent metals bonded to silicon atoms of said glass through divalent oxygen linkages or otherwise immobilized therein, by a process which involves the ion exchange of said toxic, radioactive anions with hydroxyl groups attached to said organofunctionalsiloxy groups or with hydroxyl groups attached to the hydrous polyvalent metal. Thereafter, the resulting glass now characterized by a distribution of internally bonded or immobilized, toxic, radioactive anions can be packaged in suitable containers, and disposed of as by burial, and/or they can be sintered to collapse the pores thereof prior to disposal or for producing useful radiation sources. The porous glass or a porous silica gel having said silicon-bonded organofunctionalsiloxy groups and/or said hydrous polyvalent metal oxy groups, the pores of said glass or silica gel remaining open and uncollapsed, can be used advantageously as a backfill for an underground radioactive waste burial site and as overpack in the waste disposal container. Also included is a novel method for bonding the polyvalent metal to the porous silica glass or gel by substituting the protons of the silicon-bonded hydroxyl groups thereof with an alkali metal or ammonium cation followed by displacement of said cation with the non-radioactive polyvalent metal cation.